Veneer Core
Veneer Core is produced by placing the โlinesโ of core veneers into the panel โsandwichโ so that adjacent plies having a grain direction oriented at approximate right angles to each other. Veneer core panels are relatively light in comparison with composite core panels, typically weighing about 70 pounds per 3/4โณ panel.
Veneer core offers superior physical properties than either PBC and MDF, but they may exhibit a bit more thickness variation.
Due to ever decreasing face veneer thicknesses, slight imperfections on a veneer core surface may show through or โtelegraph.โ
Veneer core may be manufactured with fir, aspen or yellow poplar, or a combination of these.
MPX core is Columbiaโs newest core innovation using extremely smooth poplar hardwood cross bands under the face and back. These poplar crossbands are peeled on state-of-the-art Meinanยฎ lathes producing the smoothest domestic all-wood core in North America.
Multi-layered core is a specialty all hardwood โEuropean style,โ high ply-count birch veneer core blank. This core is often used for decorative applications where the panel edge is revealed. Europly PLUSยฎ and DesignEdgeโข are NAUF panels. A 3/4โณ Europly PLUSยฎ panel weighs about 85 lbs. A 3/4โณ DesignEdgeโข panel weighs about 63 lbs.
Particleboard Core (PBC) is composed of wood particles bonded together with adhesive. Itโs the least expensive core option, with a smooth, void-free surface. PBC is very uniform in thickness and density, but is heavy weighing about 100 lbs per 3/4โณ panel.
Medium Density Fiberboard (MDF) is composed of wood fiber bundles bonded with adhesive. It offers a very smooth, void-free surface. MDF has greater strength and screw holding properties than particleboard and weighs around 100 lbs per 3/4โณ panel. MDF is a good choice for very thin panel applications.
Combi-Core is constructed of veneer core inner plies with MDF cross bands next to the face and back. Offers similar strength and stability to veneer core but has the void-free surface quality of MDF. This visibly reduces core veneer telegraphing.